Zirconia Ceramic Cutter Blade

 

Zirconia ceramic cutter blades are high value because of the superior performance of zirconia itself. It is mainly used as an important raw material for refractory materials, high-temperature structural materials, and electronic materials.

So, what are the requirements for zirconia ceramic cutter blade processing?

First, the thickness of the bracket in the work: the thickness of the bracket before sintering is at least 0.7mm. After sintering, it is not less than 0.4mm, which is crucial for maintaining the integrity of the Zirconia Ceramic Cutter Blade.

Second, sintering: before sintering, the slag caused by the grinding and polishing of the upper side of the bracket should be cleaned and tidy. After sintering, the size of the bracket will be 25% closed. Therefore, it is necessary to use a suitable sintering furnace. This furnace’s temperature can reach 1600 °C, especially when processing Zirconia Ceramic Cutter Blade.

Third, open the furnace: 300 °C It is important to note that there should be sufficient indoor space in the sintering work during processing. This prevents deformation. When necessary (larger long bridges), the whole sinter is made. After sintering, each support point is disconnected. After sintering, this raw material can achieve the necessary process performance. For example, it has a large compressive strength similar to 1200MPa. Zirconia ceramic plate raw materials have high compressive strength. If a crack is found, most of them are milling to cause problems. If you are interested in the zirconia ceramic plates,welcome inquiry. The use of Zirconia Ceramic Cutter Blade ensures precision in such processes.